Standard: ASTM A36, ASTM A283, ASTM A572, ASTM A656, JIS G3101 SS400, EN10025-2, DIN 17100, DIN 17102, GB/T700, GB/T1591
Surface Treatment: Oiled, black painted, shot blasted, hot dipped galvanized
Carbon steel is an alloy consisting of iron and carbon. Several other elements are allowed in carbon steel, with low maximum percentages. These elements are manganese, with a 1.65% maximum, silicon, with a 0.60% maximum, and copper, with a 0.60% maximum. Other elements may be present in quantities too small to affect its properties.
There are four types of carbon steel based on the amount of carbon present in the alloy. Lower carbon steels are softer and more easily formed, and steels with a higher carbon content are harder and stronger, but less ductile, and they become more difficult to machine and weld. Below are the properties of the grades of carbon steel we supply:
Low Carbon Steel – Composition of 0.05%-0.25% carbon and up to 0.4% manganese. Also known as mild steel, it is a low-cost material that is easy to shape. While not as hard as higher-carbon steels, carburizing can increase its surface hardness.
Medium Carbon Steel – Composition of 0.29%-0.54% carbon, with 0.60%-1.65% manganese. Medium carbon steel is ductile and strong, with long-wearing properties.
High Carbon Steel – Composition of 0.55%-0.95% carbon, with 0.30%-0.90% manganese. It is very strong and holds shape memory well, making it ideal for springs and wire.
Very High Carbon Steel - Composition of 0.96%-2.1% carbon. Its high carbon content makes it an extremely strong material. Due to its brittleness, this grade requires special handling.
|ASTM A36 Carbon Structural Steel Plate Application Fields|
|Machinery Parts||Frames||Fixtures||Bearing Plates||Tanks||Bins||Bearing Plates||Forgings|
|ASTM A36 Steel Plate Fabrication Options|
|Cold Bending||Mild Hot Forming||Punching||Machining||Welding||Cold Bending||Mild Hot Forming||Punching|
|ASTM A36 Hot Rolled Steel Plate||Chemical Compostion|
|Carbon, C||0.25 - 0.290 %|
|Copper, Cu||0.20 %|
|Iron, Fe||98.0 %|
|Manganese, Mn||1.03 %|
|Phosphorous, P||0.040 %|
|Silicon, Si||0.280 %|
|Sulfur, S||0.050 %|
|ASTM A36 Hot Rolled Steel Plate|
|Tensile Strength, Ultimate||400 - 550 MPa||58000 - 79800 psi|
|Tensile Strength, Yield||250 MPa||36300 psi|
|Elongation at Break (in 200 mm)||20.0 %||20.0 %|
|Elongation at Break (in 50 mm)||23.0 %||23.0 %|
|Modulus of Elasticity||200 GPa||29000 ksi|
|Bulk Modulus (typical for steel)||140 GPa||20300 ksi|
|Shear Modulus||79.3 GPa||11500 ksi|